| Product |
MgO (%)
min. |
Cr2O3
(%) min. |
SiO2
(%) max. |
A.P.
(%) max. |
C.C.S.
kg/cm2
(min) |
PLC at
16000C/
2 hrs. |
RUL
Ta0C
min. |
Thermal
Spalling
(Airquenching
at 10000C |
Application |
| VICS-MCH-I |
60 |
15 |
- |
22 |
400 |
± 0.5 |
1600 |
|
For general application |
| VICS-MCH-II |
65 |
10 |
- |
21 |
450 |
± 0.5 |
1600 |
|
A.O.D./V.O.D./LRF |
| VICS-MCH-III |
70 |
8 |
- |
22 |
400 |
± 0.5 |
1600 |
|
Alkali resistant brick for paper & chemical industry |
| VICS-PERIMAC |
83 |
7 |
<1 |
18 |
500 |
± 0.5 |
1700 |
+100 Cycles |
For Cement Plant rotary kiln. |
| VICS-MCDB-I |
60 |
12-14 |
1.0 |
18 |
450 |
10 |
± 0.5 |
1750 |
VOD/AOD slag zone and copper smelter |
| VICS-MCDB-II |
65 |
12-14 |
2.0 |
18 |
450 |
± 0.5 |
1750 |
|
Metal zone of VOD/AOD, bottom, free board |
| VICS-MCDB-III |
80 |
5-6 |
3.0 |
17 |
450 |
± 0.5 |
1750 |
|
BOF lining, VOD/AOD/VAD vessel RH DH vessels |
| VICS-CHM-I |
40 |
18 |
- |
24 |
300 |
± 0.5 |
1580 |
|
For general application |
| VICS-CHROME |
- |
40 |
- |
21 |
500 |
± 0.5 |
1480 |
|
Abrasion resistant quality bricks for hearth for soaking pit and reheating furnace |